Osteoblastic response to biomaterials surfaces: Extracellular matrix proteomic analysis.

The cellular response to surfaces is mediated, among other factors, by the extracellular matrix (ECM). However, little is known about the ECM proteome during mineralization. Our objective was to compare the ECM composition formed by osteoblast on different materials surfaces with proteomic analysis. Three types of biomaterial surfaces (pure titanium, anodized titanium, and zirconia) were used. Osteoblasts (MC3T3 linage) cells were cultivated on the biomaterials for 7, 14, and 21 days with the osteogenic medium. For the proteomic analysis, the specimens were washed, decellularized, and the ECM was collected. The majority of the typical ECM proteins, out of a total of 24 proteins identified, was expressed and regulated equally on the three biomaterials tested. Alpha-1,4 glucan phosphorylase was found to be down-regulated on zirconia on the seventh day, while at the same time, glycogen phosphorylase brain form was up-regulated on anodized titanium, both when compared with pure titanium (ratio: 1.06 and 0.97, respectively). And after 14 days of culture, glycogen phosphorylase brain form was downregulated on zirconia when compared with pure titanium (ratio: 0.90), suggesting the influence of material surface roughness and chemical composition on energy metabolism. Proteins related to bone development like Transforming growth factor beta-3 and Fibroblast growth factor 8 were found exclusively on pure titanium on the 21st day. Altogether, our results show a possible influence of material surfaces on the composition of ECM.

Influence of the casting processing route on the corrosion behavior of dental alloys.

Casting in the presence of oxygen may result in an improvement of the corrosion performance of most alloys. However, the effect of corrosion on the casting without oxygen for dental materials remains unknown. The aim of this study was to investigate the influence of the casting technique and atmosphere (argon or oxygen) on the corrosion behavior response of six different dental casting alloys. The corrosion behavior was evaluated by electrochemical measurements performed in artificial saliva for the different alloys cast in two different conditions: arc melting in argon and oxygen-gas flame centrifugal casting. A slight decrease in open-circuit potential for most alloys was observed during immersion, meaning that the corrosion tendency of the materials increases due to the contact with the solution. Exceptions were the Co-based alloys prepared by plasma, and the Co-Cr-Mo and Ni-Cr-4Ti alloys processed by oxidized flame, in which an increase in potential was observed. The amount of metallic ions released into the artificial saliva solution during immersion was similar for all specimens. Considering the pitting potential, a parameter of high importance when considering the fluctuating conditions of the oral environment, Co-based alloys show the best performance in comparison with the Ni-based alloys, independent of the processing route.

Are new TiNbZr alloys potential substitutes of the Ti6Al4V alloy for dental applications? An electrochemical corrosion study.

The main aim of this work was to assess the electrochemical behavior of new Ti35Nb5Zr and Ti35Nb10Zr alloys in artificial saliva at 37 °C to verify if they are indicated to be used as biomaterials in dentistry as alternatives to Ti6Al4V alloys in terms of corrosion protection efficiency of the material. Electrochemical impedance spectroscopy (EIS) experiments were carried out for different periods of time (0.5-216 h) in a three-electrode cell, where the working electrode (Ti alloys) was exposed to artificial saliva at 37 °C. The near-surface region of the alloys was investigated using x-ray photoelectron spectroscopy (XPS). All alloys exhibited an increase in corrosion potential with the immersion time, indicating the growth and stabilization of the passive film. Ti35Nb5Zr and Ti6Al4V alloys had their EIS results interpreted by a double-layer circuit, while the Ti35Nb10Zr alloy was modeled by a one-layer circuit. In general, the new TiNbZr alloys showed similar behavior to that observed for the Ti6Al4V. XPS results suggest, in the case of the TiNbZr alloys, the presence of a thicker passive layer containing a lower fraction of TiO2 phase than that of Ti6Al4V. After long-term immersion, all alloys develop a calcium phosphate phase on the surface. The new TiNbZr alloys appear as potential candidates to be used as a substitute to Ti6Al4V in the manufacturing of dental implant-abutment sets.

Effects of chemical composition on the corrosion of dental alloys.

The aim of this study was to determine the effect of the oral environment on the corrosion of dental alloys with different compositions, using electrochemical methods. The corrosion rates were obtained from the current-potential curves and electrochemical impedance spectroscopy (EIS). The effect of artificial saliva on the corrosion of dental alloys was dependent on alloy composition. Dissolution of the ions occurred in all tested dental alloys and the results were strongly dependent on the general alloy composition. Regarding the alloys containing nickel, the Ni-Cr and Ni-Cr-Ti alloys released 0.62 mg/L of Ni on average, while the Co-Cr dental alloy released ions between 0.01 and 0.03 mg/L of Co and Cr, respectively.The open-circuit potential stabilized at a higher level with lower deviation (standard deviation: Ni-Cr-6Ti = 32 mV/SCE and Co-Cr = 54 mV/SCE). The potenciodynamic curves of the dental alloys showed that the Ni-based dental alloy with >70 wt% of Ni had a similar curve and the Co-Cr dental alloy showed a low current density and hence a high resistance to corrosion compared with the Ni-based dental alloys. Some changes in microstructure were observed and this fact influenced the corrosion behavior for the alloys. The lower corrosion resistance also led to greater release of nickel ions to the medium. The quantity of Co ions released from the Co-Cr-Mo alloy was relatively small in the solutions. In addition, the quantity of Cr ions released into the artificial saliva from the Co-Cr alloy was lower than Cr release from the Ni-based dental alloys.

Effects of chemical composition on the corrosion of dental alloys

The aim of this study was to determine the effect of the oral environment on the corrosion of dental alloys with different compositions, using electrochemical methods. The corrosion rates were obtained from the current-potential curves and electrochemical impedance spectroscopy (EIS). The effect of artificial saliva on the corrosion of dental alloys was dependent on alloy composition. Dissolution of the ions occurred in all tested dental alloys and the results were strongly dependent on the general alloy composition. Regarding the alloys containing nickel, the Ni-Cr and Ni-Cr-Ti alloys released 0.62 mg/L of Ni on average, while the Co-Cr dental alloy released ions between 0.01 and 0.03 mg/L of Co and Cr, respectively.The open-circuit potential stabilized at a higher level with lower deviation (standard deviation: Ni-Cr-6Ti = 32 mV/SCE and Co-Cr = 54 mV/SCE). The potenciodynamic curves of the dental alloys showed that the Ni-based dental alloy with >70 wt% of Ni had a similar curve and the Co-Cr dental alloy showed a low current density and hence a high resistance to corrosion compared with the Ni-based dental alloys. Some changes in microstructure were observed and this fact influenced the corrosion behavior for the alloys. The lower corrosion resistance also led to greater release of nickel ions to the medium. The quantity of Co ions released from the Co-Cr-Mo alloy was relatively small in the solutions. In addition, the quantity of Cr ions released into the artificial saliva from the Co-Cr alloy was lower than Cr release from the Ni-based dental alloys.

O objetivo deste estudo foi determinar o efeito do ambiente bucal na corrosão de diferentes ligas odontológicas, utilizando métodos eletroquímicos. Os índices de corrosão foram obtidos por meio das curvas de corrente-potencial e impedância eletroquímica (EIS). O efeito de saliva artificial na corrosão de ligas odontológicas foi dependente da composição. A dissolução dos íons ocorreu em todas as amostras e os resultados foram dependentes da composição da liga. Algumas mudanças na microestrutura foram observadas durante o estudo e influenciou o comportamento corrosivo das ligas investigadas. As ligas de Ni-Cr e Ni-Cr-Ti libertaram quantidade de 0,62 mg/L de íons Ni enquanto a liga de Co-Cr liberou entre 0,01 e 0,03 mg/L. As curvas potenciodinâmicas das ligas odontológicas mostraram que as ligas a base >70 wt% de Ni obtiveram curvas similares e a liga de Co-Cr apresentou a menor densidade de corrente e em consequência uma resistência alta a corrosão quando comparada as ligas à base de Ni. A baixa resistência à corrosão também levou a maior libertação de íons de níquel para o meio e a quantidade de Co liberado pela liga de Co-Cr-Mo foi relativamente pequena nas soluções. As quantidades de Cr liberada na saliva artificial pela liga de Co-Cr foi menor que a libertação de Cr pela liga à base de Ni.